VITAMIDE® AI10BK6201CT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HxzYsf_VITAMIDE-AI10BK6201CT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® AI10BK6201CT is a Polyamide 66 (Nylon 66) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 5.0 to 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 2.3 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 65.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 52 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Break | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1 | No Break | ASTM D256 | |
| Charpy Unnotched Impact Strength | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 190 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 253 | °C | ISO 306/A50 |
| -- | 216 | °C | ISO 306/B50 |
| Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 27 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 600 | V | IEC 60112 |
| -- 2 | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2385 C | RTP Company | PUR, Unspecified | RTP |
| Teflon® PFA 345 | DuPont Fluoropolymers | PFA | Teflon® PFA |
| MAJORIS DFR918 | AD majoris | PP, Unspecified | MAJORIS |
| apigo bio® CM 1100 | API SpA | TPO (POE) | apigo bio® |
| Enable™ 20-10 Series | ExxonMobil Chemical | mPE | Enable™ |