Optix® CA-51 KC
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Plaskolite, Inc. |
| Trademark: | Optix® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hx752p_OptixCA51KC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Optix®CA-51 KC is a polymethyl methacrylate-acrylic material,. This product is available in North America or Europe,. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2830 | MPa | ASTM D638 |
| Tensile Strength | 53.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus | 2980 | MPa | ASTM D790 |
| Flexural Strength | 86.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 16 | J/m | ASTM D256 |
| Dart Drop Impact 1(3.18 mm) | 0.226 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.6 | °C | ASTM D648 |
| Vicat Softening Temperature | 93.9 | °C | ASTM D1525 |
| CLTE - Flow (-30 to 30°C) | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Geometry GB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ProTherm® 4305 | Axiall Corporation | CPVC | ProTherm® |
| Styropor® BFL 495 | BASF Corporation | PS (EPS) | Styropor® |
| COPYLENE® CR350CL-02 | Phillips 66 | PP Random Copolymer | COPYLENE® |
| Mafill® CR CT 5344 | Ravago Group | PP Copolymer | Mafill® |
| ULTEM™ LTX300B resin | SABIC Innovative Plastics | PEI | ULTEM™ |