Horda E8201
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Horda Cable Compounds |
| Trademark: | Horda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HwzUvG_Horda-E8201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
E8201 is a crosslinkable, strippable semiconductive compound, designed for EPDM rubber insulated cables and use in both dry and steam curing processes. E8201 meets the requirements as below, when optimal processing extrusion and end testing procedure are used:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ASTM D1928 |
| Mooney Viscosity (ML 1+4, 121°C) | 27 | MU | ISO 289 |
| Moisture 1 | ppm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 2(200°C) | 60/20 | % | IEC 540 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Stripping Angle | 180 | ° | |
| Stripping Force - EPR 3(23°C) | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 - 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 250 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | -10 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (135°C, 168 hr) | -30 | % | ASTM D573 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | < 2.0E+2 | ohms·cm | ASTM D257 |
| 90°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| 120°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 40.0 | °C | |
| Hopper Temperature | 50.0 - 70.0 | °C | |
| Cylinder Zone 1 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 2 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 3 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 4 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 5 Temp. | 60.0 - 110 | °C | |
| Die Temperature | 100 - 130 | °C |
| Extrusion instructions |
|---|
| Neck Temperature: 100 to 130°CHead Temperature: 100 to 130°C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| 2 . | 20 N/cm² |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE HR472 | Sasol Polymers | LLDPE | Sasol Polymers PE |
| Geon™ Bold L5000 | PolyOne Corporation | PVC Alloy | Geon™ Bold |
| Karina NATURAL PVC COMPOUND 901-25/ 1-CR-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ AF002XXC compound | SABIC Innovative Plastics | ABS | LNP™ THERMOCOMP™ |
| TECACOMP® PEEK 450 CMF white 3809 | Ensinger GmbH | PEEK | TECACOMP® |