Multilon® T-2716
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Multilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HwqAD7_MultilonT2716.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS polymer alloy, T-2700 series, Automotive series |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Transverse flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Flow : 4.00mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | 2B to B | JIS K5600 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2150 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 23°C | 54.0 | MPa | ISO 527-2/50 |
| Fracture, 23°C | 52.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture, 23°C | 110 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 84.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 35 | kJ/m² | ISO 179 |
| 23°C | 60 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 128 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 108 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 132 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ecollent™ PC/ABS | Lucent Polymers, Inc. | PC+ABS | Ecollent™ |
| Kostrate® EDGE LE | Plastic Selection Group, Inc. | TP, Unspecified | Kostrate® EDGE |
| OP - PC - Filled PC 20CCF | Oxford Polymers | PC | OP - PC - Filled |
| Celanex® 5206HG | Celanese Corporation | PET | Celanex® |
| TOTAL Polystyrene Crystal 525L | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |