MAJORIS BGR313
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HwmWQV_MAJORIS-BGR313.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BGR313 is a 30% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in natural, but other colours can be provided on request. BGR313 has been developed especially for demanding applications in various engineering sectors. BGR313 has very high rigidity and impact strength, good detergent resistance, antistatic, good dimensional stability and good creep resistance also at high temperatures. APPLICATIONS Product requiring very high overall mechanical performance such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | |||
| Vertical flow direction | 1.1 | % | |
| Flow direction | 0.16 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 5900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 41 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 159 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 143 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 164 | °C | ISO 306/A |
| -- | 135 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 150x80x2 mm |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9855A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| PRIMATOP PP CO 200 NB | Amco Polymers | PP Impact Copolymer | PRIMATOP |
| Karina NATURAL PVC COMPOUND 900-25/ 1-AYR-IS-LMP (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OmniCarb™ PC 20 UV | OMNI Plastics, LLC | PC | OmniCarb™ |
| Capilene® QC 71 E | Carmel Olefins Ltd. | PP Random Copolymer | Capilene® |