VESTAMID® HTplus M1900
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® HTplus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hwi7xc_VESTAMID-HTplus-M1900.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VESTAMID HTplus M1900 is an unreinforced, heat-stabilized polyphthalamide compound (PPA) containing a halogen-free flame retardant. It is free of red phosphorus. Due to the halogen-free flame retardant VESTAMID HTplus M1900 is especially suitable for interior parts in aircrafts, railway vehicles and ships. This compound can be used for injection molding and is especially for manufacturing parts subjected to high temperature. Parts made of VESTAMID HTplus M1900 are suitable for using in reflow soldering process. VESTAMID HTplus M1900 is supplied as spherical pellets in polyethylene packaging. Drying at 120°C for at least 4 hours before processing is recommended. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.23 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.8 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Complete Break | 3.0 | kJ/m² | |
| 23°C, Complete Break | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C, Complete Break | 24 | kJ/m² | |
| 23°C, Complete Break | 22 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 256 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 138 | °C | ISO 75-2/A |
| Melting Temperature | 300 to 315 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-0 | ||
| 0.800 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veradel® 3600P | Solvay Specialty Polymers | PESU | Veradel® |
| ELIX™ ABS H801 | ELIX Polymers, S. L. | PC+ABS | ELIX™ ABS |
| Laprene® 83F000952 | SO.F.TER. SPA | SEBS | Laprene® |
| INEOS HDPE T50-4400-119 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| POCAN® DP C 1502 000000 | LANXESS Asia/Pacific | PC+PBT | POCAN® |