FERROCON® EPP99GA02BK
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERROCON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HwcQ5P_FERROCON-EPP99GA02BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERROCON®EPP99GA02BK is a polypropylene copolymer (PP Copoly) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. FERROCON®The main features of the EPP99GA02BK are:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 | % | ASTM D955 |
| Transverse flow | 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 24.1 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 1210 | MPa | ASTM D790 |
| Tangent : 23°C | 1310 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 31.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 510 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 22.6 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 132 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.2 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+2 | ohms | ASTM D257 |
| Volume Resistivity | 3.0E+2 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| The value listed as Volume Resistivity, ASTM D257, was tested in accordance with ASTM D637.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with QARD-17.Filler Content, ASTM D2584: 21.0% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 204 - 232 | °C | |
| Middle Temperature | 216 - 260 | °C | |
| Front Temperature | 221 - 260 | °C | |
| Nozzle Temperature | 216 - 260 | °C | |
| Mold Temperature | 26.7 - 65.6 | °C | |
| Back Pressure | 0.138 - 0.345 | MPa | |
| Screw Speed | 40 - 100 | rpm | |
| Clamp Tonnage | 2.8 - 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3489 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Starpylen HZ 50E3 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| BMC 501 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| APICAL 50AV | Kaneka Corporation | Film, PI | APICAL |
| DIALAC® S710A | UMG ABS, Ltd. | ASA | DIALAC® |