Telcar® TL-86-K902A
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HwYH7s_Telcar-TL-86-K902A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Telcar TL-86-K902A is a general purpose thermoplastic elastomer designed for the industrial market. Telcar TL-86-K902A is UV stable and is suitable for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 second, injection molding | 77 | ASTM D2240 | |
| Shore A, 15 seconds, injection molding | 75 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 2.70 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 5.31 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 3.92 | MPa | ASTM D412 |
| Tensile Strength 4 | ASTM D412 | ||
| Transverse flow : Fracture | 10.8 | MPa | ASTM D412 |
| Flow : Fracture | 6.17 | MPa | ASTM D412 |
| Tensile Elongation 5 | ASTM D412 | ||
| Transverse flow : Fracture | 710 | % | ASTM D412 |
| Flow : Fracture | 280 | % | ASTM D412 |
| Tear Strength 6 | ASTM D624 | ||
| Transverse flow | 37.7 | kN/m | ASTM D624 |
| Flow | 33.4 | kN/m | ASTM D624 |
| Compression Set 7 | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | ASTM D395B |
| 70°C, 22 hr | 46 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 177 - 199 | °C | |
| Front Temperature | 182 - 204 | °C | |
| Nozzle Temperature | 188 - 210 | °C | |
| Processing (Melt) Temp | 188 - 210 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 166 - 188 | °C | |
| Cylinder Zone 2 Temp. | 171 - 193 | °C | |
| Cylinder Zone 3 Temp. | 177 - 199 | °C | |
| Cylinder Zone 5 Temp. | 182 - 204 | °C | |
| Die Temperature | 190 - 210 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Mouth die C, 510mm/min |
| 6 . | C mold, 510mm/min |
| 7 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MORETEC™ 0278G | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| BRALEN® RB 03-23 | Slovnaft Petrochemicals, s.r.o. | LDPE | BRALEN® |
| EnCom S PC 1614 R | EnCom, Inc. | PC | EnCom |
| ICORENE® 4007 | ICO Polymers EMEA, A Division of A. Schulman | PP Impact Copolymer | ICORENE® |
| apilon 52® MA-8505 | API SpA | TPU-Polyester | apilon 52® |