LNP™ LUBRICOMP™ GFL36L compound
| Category: | PSU , Polysulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HwPwqE_LNP-LUBRICOMP-GFL36L-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* GFL36L is a compound based on Polysulfone resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Low Extractable, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound GFL-4036 LE Product reorder name: GFL36L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.51 | % | ISO 294-4 |
| Flow : 24 hr | 0.26 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10300 | MPa | ASTM D638 |
| -- | 9330 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 88.9 | MPa | ASTM D638 |
| Yield | 87.0 | MPa | ISO 527-2 |
| Break | 88.9 | MPa | ASTM D638 |
| Break | 87.0 | MPa | ISO 527-2 |
| Tensile Elongation | ASTM D638, ISO 527-2 | ||
| Yield | 1.3 | % | |
| Break | 1.3 | % | |
| Flexural Modulus | |||
| -- | 8960 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 110 | MPa | ASTM D790 |
| -- | 121 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.42 | ||
| vs. Itself - Static | 0.62 | ||
| Wear Factor - Washer | 44.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 340 | J/m | ASTM D4812 |
| 23°C 3 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 14.4 | J | ASTM D3763 |
| -- | 3.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 185 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 186 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 180 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 181 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 327 to 338 | °C | |
| Middle Temperature | 338 to 349 | °C | |
| Front Temperature | 349 to 360 | °C | |
| Processing (Melt) Temp | 360 to 371 | °C | |
| Mold Temperature | 149 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Footwear GFE-1815 | S&E Specialty Polymers, LLC | PVC+NBR | S&E Footwear |
| THERMOLAST® K TF5PEN (Series: FC/AD/PE) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Nylene® 8005 HSL | Custom Resins Group | Nylon 66 | Nylene® |
| DeWAL DW 211 | DeWAL Industries | PTFE | DeWAL |
| En Chuan 6021H | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |