Order Products : sales@su-jiao.com

Makrolon® 3206

Category:	PC , Polycarbonate
Manufacturer:	Covestro - Polycarbonates
Trademark:	Makrolon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Hw6E2Y_Makrolon-3206.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
MVR (300 °C/1.2 kg) 5.0 cm³/10 min; food contact quality; high viscosity; injection molding - melt temperature 280 - 320 °C; extrusion; available in transparent, translucent and opaque colors

General Information
Features	Food Contact Acceptable High Viscosity
RoHS Compliance	RoHS Compliant
Appearance	Clear/Transparent Colors Available Opaque Translucent
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.20	g/cm³	ISO 1183
Apparent Density ¹	0.66	g/cm³	ISO 60
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	5.5	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (300°C/1.2 kg)	5.00	cm³/10min	ISO 1133
Molding Shrinkage
Across Flow	0.60 to 0.80	%	ISO 2577
Flow	0.60 to 0.80	%	ISO 2577
Across Flow : 2.00 mm ²	0.75	%	ISO 294-4
Flow : 2.00 mm ³	0.70	%	ISO 294-4
Water Absorption			ISO 62
Saturation, 23°C	0.30	%
Equilibrium, 23°C, 50% RH	0.12	%

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	111	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2350	MPa	ISO 527-2/1
Tensile Stress			ISO 527-2/50
Yield, 23°C	65.0	MPa
Break, 23°C	75.0	MPa
Tensile Strain			ISO 527-2/50
Yield, 23°C	6.3	%
Break, 23°C	130	%
Nominal Tensile Strain at Break (23°C)	> 50	%	ISO 527-2/50
Tensile Creep Modulus			ISO 899-1
1 hr	2200	MPa
1000 hr	1900	MPa
Flexural Modulus ⁴(23°C)	2350	MPa	ISO 178
Flexural Stress ⁵			ISO 178
3.5% Strain, 23°C	72.0	MPa
23°C	95.0	MPa
Flexural Strain at Flexural Strength (23°C) ⁶	7.2	%	ISO 178

Films	Nominal Value	Unit	Test Method
Gas Permeation			ISO 2556
Carbon Dioxide : 23°C, 25.4 µm	16900	cm³/m²/bar/24 hr
Carbon Dioxide : 23°C, 100.0 µm	3800	cm³/m²/bar/24 hr
Nitrogen : 23°C, 25.4 µm	510	cm³/m²/bar/24 hr
Nitrogen : 23°C, 100.0 µm	120	cm³/m²/bar/24 hr
Oxygen : 23°C, 25.4 µm	2760	cm³/m²/bar/24 hr
Oxygen : 23°C, 100.0 µm	650	cm³/m²/bar/24 hr

Flammability	Nominal Value	Unit	Test Method
Application of Flame from Small Burner - Method K and F (2.00 mm)	K1, F1		DIN 53438-1, -3
Burning Rate - US-FMVSS (> 1.00 mm)	passed		ISO 3795
Flash Ignition Temperature	480	°C	ASTM D1929
Glow Wire Test			EDF HN60 E.02
1.50 mm	850	°C
3.00 mm	850	°C
Needle Flame Test			IEC 60695-11-5
Method F : 1.50 mm	1.0	min
Method F : 2.00 mm	2.0	min
Method F : 3.00 mm	2.0	min
Method K : 2.00 mm	0.1	min
Method K : 3.00 mm	0.2	min
Self Ignition Temperature	550	°C	ASTM D1929

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion (23°C)	A1		IEC 60426
ISO Shortname	ISO 7391-PC,M,(,,)-05-9

Films	Nominal Value	Unit	Test Method
Water Vapor Transmission Rate (23°C, 85% RH, 100 µm)	15	g/m²/24 hr	ISO 15106-1

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength ⁷			ISO 7391
-30°C, Complete Break	18	kJ/m²
23°C, Partial Break	80	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-60°C	No Break
-30°C	No Break
23°C	No Break
Notched Izod Impact Strength ⁸			ISO 7391
-30°C, Complete Break	20	kJ/m²
23°C, Partial Break	75	kJ/m²
Multi-Axial Instrumented Impact Energy			ISO 6603-2
-30°C	75.0	J
23°C	65.0	J
Multi-Axial Instrumented Impact Peak Force			ISO 6603-2
-30°C	6700	N
23°C	5800	N

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	142	°C	ISO 75-2/B
1.8 MPa, Unannealed	130	°C	ISO 75-2/A
Glass Transition Temperature ⁹	150	°C	ISO 11357-2
Vicat Softening Temperature
--	150	°C	ISO 306/B50
--	151	°C	ISO 306/B120
Ball Pressure Test (141°C)	Pass		IEC 60695-10-2
CLTE			ISO 11359-2
Flow : 23 to 55°C	6.5E-5	cm/cm/°C
Transverse : 23 to 55°C	6.5E-5	cm/cm/°C
Thermal Conductivity ¹⁰(23°C)	0.20	W/m/K	ISO 8302
RTI Elec (1.50 mm)	125	°C	UL 746
RTI Imp (1.50 mm)	115	°C	UL 746
RTI Str (1.50 mm)	125	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+16	ohms	IEC 60093
Volume Resistivity (23°C)	1.0E+16	ohms·cm	IEC 60093
Electric Strength (23°C, 1.00 mm)	34	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	3.10
23°C, 1 MHz	3.00
Dissipation Factor			IEC 60250
23°C, 100 Hz	5.0E-4
23°C, 1 MHz	9.5E-3
Comparative Tracking Index			IEC 60112
Solution A	250	V
Solution B	125	V

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.50 mm	HB
0.360 mm	V-2
Glow Wire Flammability Index			IEC 60695-2-12
0.750 mm	875	°C
1.50 mm	875	°C
3.00 mm	930	°C
Glow Wire Ignition Temperature			IEC 60695-2-13
0.750 mm	875	°C
1.50 mm	875	°C
3.00 mm	900	°C
Oxygen Index ¹¹	27	%	ISO 4589-2

Optical	Nominal Value	Unit	Test Method
Refractive Index ¹²	1.586		ISO 489
Transmittance			ISO 13468-2
1000 µm	89.0	%
2000 µm	89.0	%
3000 µm	88.0	%
4000 µm	87.0	%
Haze (3000 µm)	< 0.80	%	ISO 14782

Note Message
1 .	Pellets
2 .	60x60x2 mm, 500 bar
3 .	60x60x2 mm, 500 bar
4 .	2.0 mm/min
5 .	2.0 mm/min
6 .	2 mm/min
7 .	Based on ISO 179-1eA, 3 mm
8 .	Based on ISO 180-A, 3 mm
9 .	10°C/min
10 .	Cross-flow
11 .	Procedure A
12 .	Method A

Resin Grade	Manufacturer	Category	Trademark
megol® A 60/A1	API SpA	SEBS	megol®
Starex VE-0857	SAMSUNG SDI CO., LTD.	ABS	Starex
Westlake LDPE EF606	Westlake Chemical Corporation	LDPE	Westlake LDPE
AIE PA66 60G5F	Asia International Enterprise (Hong Kong) Limited	Nylon 66	AIE PA66
Sylvin 8600-85 Brown 7417	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin