LNP™ THERMOCOMP™ MX85738 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HvlFGG_LNP-THERMOCOMP-MX85738-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MX85738 is a compound based on Polypropylene resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-M-85738 Product reorder name: MX85738 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.10 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7760 | MPa | ASTM D638 |
| Tensile Strength (Break) | 66.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 6410 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 149 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen 2152HOXP | LyondellBasell Industries | PP Homopolymer | Moplen |
| Durepol® PBT A3 FR NTLA010 BT329 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| HONES® PBT F0 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PBT | HONES® |
| LNP™ VERTON™ RV007ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| LTP ZE-2150 | Chengdu Letian Plastics Co., Ltd | PPS, Linear | LTP |