CYCOLOY™ CM8622 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HuV6Iy_CYCOLOY-CM8622-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CYCOLOY CM8622 is a high heat PC/ABS blend offering high modulus, low CTE, good practical Impact with good aesthetics. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 | g/cm³ | ASTM D792 |
| -- | 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Across Flow 2 | 0.40 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.20 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 3600 | MPa | ASTM D638 |
| -- | 3600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 47.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/5 |
| Break 5 | 60.0 | MPa | ASTM D638 |
| Break | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 3.4 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/5 |
| Break 7 | 55 | % | ASTM D638 |
| Break | 50 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 3650 | MPa | ASTM D790 |
| -- 9 | 3600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C 11 | 8.0 8.0 | kJ/m² | ISO 179/1eA |
| -30°C | 8.0 | kJ/m² | ISO 179/2C |
| 23°C 12 | 12 12 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength | |||
| -30°C 13 | 100 100 | kJ/m² | ISO 179/1eU |
| -30°C | 100 | kJ/m² | ISO 179/2U |
| 23°C 14 | 110 110 | kJ/m² | ISO 179/1eU |
| 23°C | 110 | kJ/m² | ISO 179/2U |
| Notched Izod Impact | |||
| -30°C | 90 | J/m | ASTM D256 |
| 23°C | 250 | J/m | ASTM D256 |
| -30°C 15 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 16 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 1500 | J/m | ASTM D4812 |
| 23°C | 1700 | J/m | ASTM D4812 |
| -30°C 17 | 140 | kJ/m² | ISO 180/1U |
| 23°C 18 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 50.0 | J | ASTM D3763 |
| -- | 85.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 19 | 129 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 112 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 20 | 112 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/A50 |
| -- | 133 | °C | ISO 306/B50 |
| -- | 134 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 5.1E-5 | cm/cm/°C | |
| Flow : -30 to 80°C | 5.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 7.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 265 to 290 | °C | |
| Front Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 260 to 290 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 sp=62mm |
| 14 . | 80*10*4 sp=62mm |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 |
| 19 . | 80*10*4 mm |
| 20 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultradur® B 2300 G6 HR LS BK15045 | BASF Corporation | PBT | Ultradur® |
| NITRIFLEX NP-3083 | NITRIFLEX | NBR | NITRIFLEX |
| Gallonprene® GP420-6503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| InvisiSil™ IVS4752 | Momentive Performance Materials Inc. | Silicone | InvisiSil™ |
| Lucky Enpla LAY3003 | Lucky Enpla Co LTD | PC+PBT | Lucky Enpla |