SCHULAMID® 612 GF33
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HuFA4g_SCHULAMID-612-GF33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% glass fiber reinforced, Polyamide 612 compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Saturation, 23°C) | 1.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 8050 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 165 | 122 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.6 | 4.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(23°C) | 8700 | -- | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 235 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength (23°C) | 3.40 | -- | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 8.0 | -- | kJ/m² | |
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 9.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | 50 | -- | kJ/m² | |
| -30°C | 55 | -- | kJ/m² | |
| 23°C | 60 | 70 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 216 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 199 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 214 | -- | °C | ISO 306/A50 |
| -- | 209 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 675 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 725 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR WC 0587-21 BE1 RoHS | PolyOne Corporation | PP, Unspecified | Maxxam™ FR |
| RTP PP 30 GF | RTP Company | PP, Unspecified | RTP |
| Gallonprene® GP520-6002 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| INNOPOL® PP CS 2-4630 FR | Inno-Comp Ltd. | PP Impact Copolymer | INNOPOL® PP |
| ISOTHANE® G1085AU-L | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |