Infino WP-1041
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hu40Xk_Infino-WP-1041.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow PC/ABS material that can be used for automobile R/G door handle |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 250°C/10.0 kg | 35 | g/10 min | |
| 250°C/2.16 kg | 4.0 | g/10 min | |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.50 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 103 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 1870 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 48.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break 3 | 39.0 | MPa | ASTM D638 |
| Break | 22.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 25 | % | ASTM D638 |
| Break | 22 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1900 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 66.0 | MPa | ASTM D790 |
| -- 8 | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 47 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 440 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 270 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 540 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 390 | J/m | ASTM D256 |
| 23°C 10 | 44 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 11(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 120 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 112 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 119 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 93.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 107 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 109 | °C | ISO 306/B50 |
| CLTE - Flow (40 to 100°C) | 8.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 85.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 210 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.981 to 2.45 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| 11 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 7536 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Softflex® 6001 | Network Polymers, Inc. | TPV | Softflex® |
| apigo® 8376 BS/65 | API SpA | TPO (POE) | apigo® |
| Sylvin 8480-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTOPLAST XU 425NGY146 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |