INFUSE™ 9817
| Category: | OBC , Olefin Block Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INFUSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HtNgtT_INFUSE-9817.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INFUSE™ 9817 Olefin Block Copolymer is a high performance olefin block copolymer that offers excellent performance in durable, flexible injection molded industrial and consumer goods. INFUSE 9817 has a higher set up temperature, which allows for faster injection molding cycle times. In addition, its high crystallization temperature and lower density drive to lower production cost by reducing cycle time and reducing part weight. Main Characteristics:
Complies with
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.877 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant (Compression Molded) | 2.31 | MPa | ASTM D638 |
| Tensile Strength (Break, Compression Molded) | 7.00 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 1500 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 7.00 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1700 | % | ASTM D412 |
| Tear Strength | 31.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 21°C | 15 | % | |
| 70°C | 58 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 120 | °C | Internal Method |
| TMA 1(1.00 mm) | 95 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 1N, 5°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA I XCF-0.3 | ROMPETROL PETROCHEMICALS S.R.L. | LDPE | MIDILENA I |
| YUPLENE® BT3500 | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| MAJORIS EC380 | AD majoris | PP, Unspecified | MAJORIS |
| Celanex® 5206HG | Celanese Corporation | PET | Celanex® |
| Hifax CA1110 G3 1740 | LyondellBasell Industries | TPO (POE) | Hifax |