Durethan® BKV 25 F30 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HtEUsZ_DurethanBKV25F30000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 25 % glass fibers, injection molding, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.60 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.60 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | -- | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.30 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.10 | -- | % | ISO 2577 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | 7300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | 90.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.3 | 4.4 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 10000 | 7000 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 230 | 155 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 2.5 | 4.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 8 | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GFHR, 14-110, GF25 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Admissible Residence Time at Tmax | > 10.0 | min | |
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | 50 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | 55 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | 10 | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 45 | 50 | kJ/m² | ISO 180/1U |
| 23°C | 50 | 55 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 1.90 | -- | J | ISO 6603-2 |
| 23°C | 3.00 | -- | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 900 | -- | N | ISO 6603-2 |
| 23°C | 1000 | -- | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | -- | °C | ISO 306/B120 |
| Melting Temperature 9 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 4.1E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 3.4E+14 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.400 mm | V-0 | -- | UL 94 | |
| 1.00 mm | V-0 5VA | -- | UL 94 | |
| 3.00 mm | V-0 5VA | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.400 mm | 960 | -- | °C | IEC 60695-2-12 |
| 0.800 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.400 mm | 850 | -- | °C | IEC 60695-2-13 |
| 0.800 mm | 775 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 775 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 850 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | US-FMVSS302 |
| 9 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ASA AE77 | Techno Polymer America, Inc. | ASA | TECHNO ASA |
| Supol HT121E | LyondellBasell Industries | PP Copolymer | Supol |
| VAMPAMID HT 3028 V0 | Vamp Tech | PPA | VAMPAMID |
| Lucky Enpla LGF3152F | Lucky Enpla Co LTD | PBT | Lucky Enpla |
| MAJORIS HN067 | AD majoris | PP Copolymer | MAJORIS |