Order Products : sales@su-jiao.com
CERTENE™ LLBF-322F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HstEP6_CERTENE-LLBF-322F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLBF-322F is a certified prime grade butane linear low density, designed to blown film and cast film used in general purpose packaging. LLBF-322F features excellent improved stiffness. It could be used alone or as a component in packaging and industrial film, with higher level of antiblock (7,500 ppm) and slip (1.500 ppm) additives. LLBF-322F complies with FDA regulation 21CFR 177.1520(c3).1a / 3.2a, and most international regulations for use in contact with food. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.7 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy (25 µm) | 0.450 | J | Internal method |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 155 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 154 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm | 8.30 | MPa | ASTM D882 |
| TD : Yield, 25 µm | 8.10 | MPa | ASTM D882 |
| MD : Break, 25 µm | 39.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 19.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 520 | % | ASTM D882 |
| TD : Break, 25 µm | 680 | % | ASTM D882 |
| Dart Drop Impact (25 µm) | 62 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 37 | g | ASTM D1922 |
| TD : 25 µm | 260 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 124 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 81 | ASTM D2457 | |
| Haze (25.0 µm) | 5.4 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film, melt temperature 395-430°F (200-220°C), blow-up-ratio 2.5 :1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMPLIFY™ TY 3351 | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| BUPLEN® 6531 | LUKOIL Bulgaria Ltd. | PP Homopolymer | BUPLEN® |
| Eltex® MED PH23T630 | INEOS Olefins & Polymers Europe | LDPE | Eltex® MED |
| Kingfa JH950-402 | Kingfa | PC+ABS | Kingfa |
| Petrothene® LP540200X03 | LyondellBasell Industries | HDPE | Petrothene® |