Kepital® FG2025
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HsgFr9_Kepital-FG2025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium-high viscosity grade for general injection molding. It was reinforced with glass fiber, and so suitable for parts requiring very high stiffness, fatigue resistance, creep resistance and heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 7.0 | g/10 min | ASTM D1238 |
| -- | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 2.00 mm | 0.50 | % | ASTM D955 |
| 3.00 mm | 0.50 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 152 | MPa | ASTM D638 |
| Yield, 23°C | 160 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8850 | MPa | ASTM D790 |
| 23°C | 8250 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 212 | MPa | ASTM D790 |
| 23°C | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 164 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 162 | °C | ISO 75-2/A |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| CLTE - Flow (20 to 80°C) | 2.0E-5 to 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 23 | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® HJ4012 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| BJB Polyurethane WC-540 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| DIOSHY® TPO F955D-OS | DIOSHY Co.,Ltd. | TPO (POE) | DIOSHY® |
| Geon™ Vinyl Rigid Extrusion L4857 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Petrothene® NA272130 | LyondellBasell Industries | MDPE | Petrothene® |