LNP™ STAT-LOY™ 93000LTH compound
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HseMVe_LNP-STAT-LOY-93000LTH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY 93000LTH is a compound based on Acrylic resin. Added features of this material include: Antistatic, Transparent and Formulation Locked. Also known as: LNP* STAT-LOY* Compound 93000LTH Product reorder name: 93000LTH |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1790 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 1470 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 47.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 670 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 66.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+9 to 1.0E+11 | ohms·cm | ASTM D257 |
| Static Decay 6 | < 1.0 | sec | FTMS 101B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PP pp9 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Adell Polyamide AN-18 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Cevian® SER240 | PlastxWorld Inc. | ABS | Cevian® |
| Fiberfil® J-69/20/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Shida 030 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | SBS | Shida |