Braskem PP CP 145
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HsbdG6_Braskem-PP-CP-145.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: CP 145 is a high melt flow rate heterophasic copolymer for high perfomance injection moulding machines. It features high productivity in thin-walled parts and excellent organoleptic properties, once it is a reactor grade. Applications: Household; Thin-walled parts; Easy mould filling; Packages with excelent organoleptic properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 45 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 79 | ASTM D785 | |
| R-Scale | 79 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 26.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1300 | MPa | ASTM D790 |
| Injection Molded | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 40 | J/m | ASTM D256 |
| 23°C, Injection Molded | 80 | J/m | ASTM D256 |
| -20°C, Injection Molded | 3.9 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 6.4 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 110 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 57.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 149 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miflon® 3112 | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| Shandong Aobang TPU-Polyester 95-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| VINIKA® D2151A | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | VINIKA® |
| 4MID® 9A22115 HR | 4Plas | Nylon 66 | 4MID® |
| Leona™ WG143 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |