Versalloy™ HC 9210-70N Datasheet,TPE,PolyOne Corporation-SHANGHAI SUSHENG

Message
Versalloy™XL 9070-1 is a TPV alloy with strong fluidity and surface aesthetics, suitable for a variety of applications. Very suitable for long and narrow runners Very strong coloring ability It can be bonded to polypropylene by overlapping molding Excellent surface aesthetics

General Information
Features	Non-phthalate plasticizer Recyclable materials Workability, good Good coloring High liquidity Halogen-free Excellent appearance
Uses	overmolding Thin wall parts Soft touch application Soft handle Medical/nursing supplies
Agency Ratings	USP Class VI
RoHS Compliance	RoHS compliance
Appearance	Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.888	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	70		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress			ASTM D412
100% strain, 21°C	2.45	MPa	ASTM D412
300% strain, 23°C	3.52	MPa	ASTM D412
Tensile Strength (Break, 23°C)	5.38	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	590	%	ASTM D412
Tear Strength	31.5	kN/m	ASTM D624
Compression Set			ASTM D395B
23°C, 22 hr	23	%	ASTM D395B
70°C, 22 hr	42	%	ASTM D395B
100°C, 22 hr	53	%	ASTM D395B

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 11200 sec^-1)	5.80	Pa·s	ASTM D3835

Additional Information
Versalloy™ HC 9210-70N can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.Municipality waste stream recycle code is "7" which is designated for "Other".Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.

Additional Information

Versalloy™ HC 9210-70N can be recycled as a filler or impact modifier for polyolefins, or can be recycled by grinding and reintroduction to the molding process. Similar to PP or PE recycling process, if separated appropriately, it can be recycled many times.Municipality waste stream recycle code is "7" which is designated for "Other".Please contact GLS Thermoplastic Elastomers for a copy of our Recyclability Compliance letter.

Injection	Nominal Value	Unit
Suggested Max Regrind	20	%
Rear Temperature	149 - 188	°C
Middle Temperature	160 - 199	°C
Front Temperature	171 - 210	°C
Nozzle Temperature	171 - 210	°C
Mold Temperature	15.6 - 26.7	°C
Back Pressure	0.00 - 0.689	MPa
Screw Speed	50 - 100	rpm

Injection instructions
以聚丙烯 (PP) 为基础的色母料最适合 Versalloy™ XL 9070-1 着色。使用熔体流动速率较高（范围为 25 - 40 克/10 分钟）的色母料，则能达到较好的颜色分散效果。典型的色母料用量为 1% 至 5%（重量）。不应采用以 PVC 为基础的色母料。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versalloy™ XL 9070-1 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Versalloy™ XL 9070-1 具有良好的熔体稳定性。如果机器闲置十五 (15) 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：300 - 700 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒

Injection instructions

以聚丙烯 (PP) 为基础的色母料最适合 Versalloy™ XL 9070-1 着色。使用熔体流动速率较高（范围为 25 - 40 克/10 分钟）的色母料，则能达到较好的颜色分散效果。典型的色母料用量为 1% 至 5%（重量）。不应采用以 PVC 为基础的色母料。色母料是否适用，应由用户通过试验来最终确定。在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versalloy™ XL 9070-1 可利用高达 20% 的回收料同时其性能所受影响却极小，但该回收料必须是未受到污染的。为了最大限度地减小模塑期间其性能所受的影响，熔体温度应维持得尽可能低。回收料的有效性应由用户最终确定。Versalloy™ XL 9070-1 具有良好的熔体稳定性。如果机器闲置十五 (15) 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 5 英寸/秒第一阶段 - 提升压力：300 - 700 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：4 - 10 秒保持时间（薄部件）：1 - 3 秒

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versalloy™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HsKArR_Versalloy-HC-9210-70N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
POLYSTONE® M slide AST	Röchling Engineering Plastics SE & Co. KG	UHMWPE	POLYSTONE®
Radilon® A RV350LW 358 NER 4789	Radici Plastics	Nylon 66	Radilon®
Kepital® FG1025	KEP Americas	Acetal (POM) Copolymer	Kepital®
Hyundai EP Matt MS102/Natural	HYUNDAI EP Co., Ltd.	Polyolefin, Unspecified	Hyundai EP Matt
3M™ Dyneon™ PTFE Compound TF 6262	3M Advanced Materials Division	PTFE	3M™ Dyneon™ PTFE Compound