KumhoSunny ABS HFA456
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hrigit_KumhoSunny-ABS-HFA456.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HFA456 is non-halogenand enviromental ABS resin. It has balance flow properties,mechanical properties and heat resistance. HFA456 is mainly used in consumer electronics as camcorder, digital camera, PSP etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 65 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 250 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 76.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 86.0 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 2.10 mm | V-2 | ||
| 3.20 mm | V-2 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C | |
| Processing (Melt) Temp | 200 to 210 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC3MF3-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| XANTAR® RX 2121 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Ecoflex® F Blend C1200 | BASF Corporation | Copolyester | Ecoflex® |
| Karina WHITE PVC COMPOUND -E818-10/23-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS FFR091 | AD majoris | PP, Unspecified | MAJORIS |