LEXAN™ 3414R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HreEdq_LEXAN-3414R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% GR, provides improved mechanical properties and UL94V-1 rated at 0.058". Internal mold release added. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Specific Volume | 0.658 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.20 | % | Internal Method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.12 | % | |
| Equilibrium, 23°C | 0.23 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 93 | ||
| R-Scale | 119 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 125 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 9650 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 186 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 32.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 6.78 | J | ASTM D3029 |
| Tensile Impact Strength 5 | 67.2 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 154 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 146 | °C | |
| Vicat Softening Temperature | 166 | °C | ASTM D1525 6 |
| CLTE - Flow (-40 to 95°C) | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1050 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.53 | ||
| 60 Hz | 3.53 | ||
| 1 MHz | 3.48 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.3E-3 | ||
| 60 Hz | 1.3E-3 | ||
| 1 MHz | 6.7E-3 | ||
| Arc Resistance 7 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.12 mm | V-1 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Nozzle Temperature | 310 to 332 | °C | |
| Processing (Melt) Temp | 316 to 338 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Type S |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PS-GP1 | Polymer Resources Ltd. | PS (HIPS) | PRL |
| TAROMID A 280 H G6 X0 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| G-Lex 19 PC | Gardiner Compounds Ltd. | PC | G-Lex |
| MAJORIS EW251 - 7818/5 | AD majoris | PP, Unspecified | MAJORIS |
| Plaslube® HTN 01400 BK | Techmer Engineered Solutions | Nylon, Unspecified | Plaslube® |