Geon™ CPVC EE105
| Category: | CPVC , Chlorinated Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ CPVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HrZl7z_Geon-CPVC-EE105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon EE105 CPVC is an extrusion grade rigid compound ideally suited for a variety of applications. EE105 offers excellent electrical properties, chemical resistance and is designed for applications where enhanced resistance at elevated temperatures is needed. EE105 demonstrates ease of processing with excellent thermal stability. All colors of EE105 are UL certified and are made with virgin materials. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec, 3.18 mm) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 3.18 mm, Compression Molded) | 2240 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 23°C, 3.18 mm, Compression Molded) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 23°C, 3.18 mm) | 24 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.18 mm) | 2410 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.18 mm) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drop Impact Resistance 4(23°C) | 66.7 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 3.18 mm | 111 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 105 | °C | |
| CLTE - Flow | 7.2E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.02 to 3.05 mm) | 105 | °C | UL 746 |
| RTI Imp (1.02 to 3.05 mm) | 105 | °C | UL 746 |
| RTI Str (1.02 to 3.05 mm) | 105 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| High Amp Arc Ignition (HAI) (3.05 mm) | 0.00 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| > 1.02 mm | V-0 | ||
| > 1.52 mm | 5VA |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 191 to 199 | °C |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | Procedure A, C.125 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9979-75 Grey 9222 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| BJB Silicone TC-5005 A/B-C | BJB Enterprises, Inc. | Silicone | BJB Silicone |
| DEXFLEX® 711 | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| OXPEKK® MG240C | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |
| Hostacom PPU X9067HS 101174 | LyondellBasell Industries | PP Copolymer | Hostacom |