LIHAN® B7010
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HrUhWQ_LIHAN-B7010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LIHAN® B7010 is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.10 to 0.30 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 to 1.2 | -- | % | ISO 62 |
| Water Content | 3.0 to 5.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 115 | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 220 | 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 13000 | 9000 | MPa | ISO 178 |
| Flexural Stress | 300 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 16 | 25 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature | 220 | -- | °C | DSC |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | ASTM D257 |
| Dielectric Strength | 17 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.59 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3569 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sunny® PBT EN225 | Guangdong Shunde Shunyan New Material Co., Ltd. | PBT | Sunny® |
| ColorRx® ACR-0100HIRX | LTL Color Compounders, Inc. | Acrylic, Unspecified | ColorRx® |
| POCAN® B 2505 000000 | LANXESS GmbH | PBT | POCAN® |
| DAI-EL™ G-7201 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |