Tisakril® ABS 15 GFR
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Tisan |
| Trademark: | Tisakril® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HqR7op_Tisakril-ABS-15-GFR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tisakril® ABS 15 GFR is an Acrylonitrile Butadiene Styrene (ABS) material filled with 15% glass fiber. It is available in Africa & Middle East or Europe for injection molding. Primary attribute of Tisakril® ABS 15 GFR: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Molding Shrinkage | < 1.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.50 | % | ISO 62 |
| Ash Content | 15 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 70.0 | MPa | |
| Break | 69.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 4.8 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 7.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | 108 | °C | ISO 306/B120 |
| Melting Temperature | 165 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 160 to 180 | °C | |
| Mold Temperature | 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® C320MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Adstif EA600P | LyondellBasell Industries | PP Impact Copolymer | Adstif |
| DINALON® B2S25 V2-7035 | Grupo Repol | Nylon 6 | DINALON® |
| Hostaform® C 9021 SW | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| POCAN® BF 4212 000000 | LANXESS Asia/Pacific | PBT | POCAN® |