Plaslube® PEEK CF15 TL15 A 907 BK MB
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HqIEmg_Plaslube-PEEK-CF15-TL15-A-907-BK-MB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plaslube® PEEK CF15 TL15 A 907 BK MB is a Polyetheretherketone (PEEK) product filled with carbon fiber. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 179 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 262 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 299 | °C | ASTM D648 |
| CLTE - Flow | 1.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 360 to 388 | °C | |
| Middle Temperature | 360 to 388 | °C | |
| Front Temperature | 360 to 388 | °C | |
| Processing (Melt) Temp | 360 to 382 | °C | |
| Mold Temperature | 177 to 218 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2645 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| VAMPSULF 0024 V2 | Vamp Tech | PSU | VAMPSULF |
| Cri-Line HFLT-618-65 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| DOMAMID® A1-113-V60-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| SD POLYCA™ CF5301V | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |