Desmopan® DP 9648DU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HqH65v_Desmopan-DP-9648DU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion- and injection molding grade; with special UV stabilizers; transparent up to 6 mm wall thickness; very good hydrolysis and microbial resistance; Application; Ski boot shells; Hoses, non-reinforced |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 94 | ||
| Shore D | 48 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | DIN 53504 | ||
| Break, 23°C | 51.8 | MPa | |
| 10% Strain, 23°C | 5.10 | MPa | |
| 50% Strain, 23°C | 11.7 | MPa | |
| 100% Strain, 23°C | 15.8 | MPa | |
| 300% Strain, 23°C | 31.8 | MPa | |
| Tensile Strain (Break, 23°C) | 430 | % | ISO 527-2 |
| Flexural Modulus 2(23°C) | 60.0 | MPa | ISO 178 |
| Abrasion Resistance (23°C) | 20.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 860 | MPa | |
| 20°C | 133 | MPa | |
| 60°C | 52.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 33 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3(23°C) | 110 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 38 | % | |
| 70°C, 24 hr | 44 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 215 to 235 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Melt Temperature | 200 to 235 | °C |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC2TF1-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Hanwha Total PP CI72W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Petrothene® NA345 | LyondellBasell Industries | LDPE | Petrothene® |
| Sylvin 8205-70UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ 1010 resin | SABIC Innovative Plastics | PEI | ULTEM™ |