SIBUR Synthetic Rubber SKN 3345 E
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | SIBUR, LLC |
| Trademark: | SIBUR Synthetic Rubber |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hq7yuo_SIBUR-Synthetic-Rubber-SKN-3345-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SKN 3345 E is essentially an acrylonitrile (31-35 %) and 1,3-butadiene copolymer obtained by emulsion polimerization method at a temperature of 32 °C with the use of phytogenous fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium Mooney viscosity, medium content of acrylonitrile, heightened oil resistance. Application The manufacturing of cables, packing, sleeve gaskets, fuel hoses, roll coatings, technical plates, rubberized materials, belts, sealants, adhesives, shoe soles, plastic modification. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 100°C) | 42 - 48 | MU | Internal method |
| Acrylonitrile Content | 31.0 - 35.0 | % | Internal method |
| Ash Content | % | Internal method | |
| Volatile Matter | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | > 22.5 | MPa | Internal method |
| Tensile Elongation 2(Break) | > 450 | % | Internal method |
| Additional Information |
|---|
| Recipe (Mass fraction): Rubber = 100.0 Technical stearic acid acc. GOST 6484, grades T-18 or T-32 = 1.0 Dry zink oxide acc. GOST 202, grade BCOM = 3.0 Vulcanizing accelerator TBBS acc. Specifications TY 2491-055-05761637 = 0.7 Carbon black acc. GOST 7885, grade P-324 = 40.0 Technical sulfur acc. GOST 127.4, grade 9995 or 9990, class 1 or 2 = 1.5 Total = 146.2 |
| Note Message | |
|---|---|
| 1 . | Vulcanization mode of samples: 142° × 50 min. |
| 2 . | Vulcanization mode of samples: 142° × 50 min. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA ABS 4135 | MBA Polymers | ABS | MBA ABS |
| VECTRA® A625 | Celanese Corporation | LCP | VECTRA® |
| VAMPTER 1026 V0 | Vamp Tech | PBT | VAMPTER |
| Bergamid™ A70 G50 HW EBONY 3278 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| LUVOCOM® 1105-8739/BL | Lehmann & Voss & Co. | PEEK | LUVOCOM® |