ULTEM™ 3452 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HppvXY_ULTEM3452resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 45% Glass fiber and mineral filled, enhanced flow Polyetherimide (Tg 217C) with enhanced dimensional stability. Resin is RoHS compliant. UL94 V0 and 5VA listing in recognized colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.25 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 12000 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 4.4 | kJ/m² | ISO 179/1eA |
| 23°C | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | ISO 179/1eU |
| 23°C | 14 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 5 | ISO 180/1A | ||
| -30°C | 4.9 | kJ/m² | ISO 180/1A |
| 23°C | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | 13 | kJ/m² | ISO 180/1U |
| 23°C | 14 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 207 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 200 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50, ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 3.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.70 | IEC 60250 | |
| 60 Hz | 3.70 | IEC 60250 | |
| 1 MHz | 3.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.010 | IEC 60250 | |
| 60 Hz | 0.010 | IEC 60250 | |
| 1 MHz | 0.015 | IEC 60250 | |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.770 mm | V-0 | UL 94 | |
| 3.00 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 350 - 400 | °C | |
| Middle Temperature | 360 - 410 | °C | |
| Front Temperature | 370 - 420 | °C | |
| Nozzle Temperature | 360 - 410 | °C | |
| Processing (Melt) Temp | 370 - 410 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1200-65D | RTP Company | TPU-Polyester | RTP |
| Vinnolit® MP 8058 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| ATTANE™ SL 4102G | The Dow Chemical Company | ULDPE | ATTANE™ |
| Fainplast PVC MPH 80 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hangzhou Plastic PS/PVDC/PE | Hangzhou Plastic Industry Co., Ltd. | Film, PS/PVDC/PE | Hangzhou Plastic |