SAXAMID™ 126F6T3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HogA8C_SAXAMID-126F6T3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 126F6T3 is a polyamide 6 injection-molding-grade reinforced with 30 % glass fibres and 15 % PTFE. Because of its high strength and stiffness this grade is often used for stressed parts requiring low friction - low friction coefficients result in very good wear resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8100 | MPa | ISO 178 |
| Flexural Stress 2 | 268 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 76 | kJ/m² | |
| 23°C | 82 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 75 | kJ/m² | |
| 23°C | 79 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 209 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 216 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® EVA 802 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| Bergadur™ PB40 Mi25 natur SO | PolyOne Corporation | PBT | Bergadur™ |
| Andur 6 DPLM | Anderson Development Company | PUR-Ester/TDI | Andur |
| Elastollan® C70AW | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyester | Elastollan® |
| Sylvin 4200-85 Green 3212 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |