GLS PP ZT79
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HoU5sa_GLS-PP-ZT79.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP TALC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 to 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | > 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 28.0 to 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 8.0 | % | ASTM D638 |
| Flexural Modulus | 2400 to 2800 | MPa | ASTM D790 |
| Flexural Strength | 42.0 to 48.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 30 to 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 79.0 to 80.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 32.0 to 64.0 | °C | |
| Injection Pressure | 65.0 to 105 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 96257 | RTP Company | PC | RTP |
| NILAMID® A3 J20 | Nilit Plastics | Nylon 66 | NILAMID® |
| DuraSurf™ E801 | Crown Plastics | HDPE, HMW | DuraSurf™ |
| Karina CLEAR PVC COMPOUND -E 80/205-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Axiall PVC 1801 | Axiall Corporation | PVC, Flexible | Axiall PVC |