Generic Epoxy
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HoDbGd_Generic-Epoxy.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Epoxy This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.492 to 2.00 | g/cm³ | ASTM D792 |
| 23°C | 0.994 to 1.43 | g/cm³ | ISO 1183 |
| -- | 0.787 to 1.81 | g/cm³ | ASTM D1505 |
| Apparent Density | 1.04 to 1.61 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (23°C) | 0.010 to 0.76 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.060 to 0.41 | % | |
| Saturation, 23°C | 0.20 to 0.87 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 73 to 92 | ASTM D2240 | |
| 23°C | 79 to 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 186 to 18400 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield, 23°C | 10.9 to 180 | MPa | ASTM D638 |
| Yield, 23°C | 30.0 to 76.0 | MPa | ISO 527-2 |
| Break, 23°C | 13.4 to 247 | MPa | ASTM D638 |
| Ultimate, 23°C | 45.7 to 53.0 | MPa | ASTM D638 |
| 23°C | 0.00621 to 83.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 0.40 to 6.7 | % | |
| Break, 23°C | 0.63 to 23 | % | |
| Flexural Modulus (23°C) | 1.17 to 12700 | MPa | ASTM D790 |
| Flexural Strength | |||
| 23°C | 0.00686 to 179 | MPa | ASTM D790 |
| 23°C | 85.0 to 100 | MPa | ISO 178 |
| Yield, 23°C | 26.4 to 252 | MPa | ASTM D790 |
| Break, 23°C | 57.1 to 62.4 | MPa | ASTM D790 |
| Compressive Modulus | 21.6 to 2800 | MPa | ASTM D695 |
| Compressive Strength (23°C) | 16.7 to 201 | MPa | ASTM D695 |
| Shear Strength (23°C) | 3.90 to 53.5 | MPa | ASTM D732 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 17.2 to 56.5 | MPa | ASTM D412 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 11 to 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 48.8 to 243 | °C | |
| 1.8 MPa, Unannealed | 44.3 to 245 | °C | |
| Continuous Use Temperature | 68.8 to 157 | °C | ASTM D794 |
| Glass Transition Temperature | |||
| -- | 36.1 to 228 | °C | ASTM E1356 |
| -- | 51.8 to 171 | °C | DSC |
| CLTE - Flow | 5.8E-6 to 9.2E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | |||
| 23°C | 0.062 to 0.86 | W/m/K | ASTM C177 |
| 23°C | 0.20 to 0.42 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.0E+10 to 1.5E+16 | ohms | ASTM D257 |
| Volume Resistivity | |||
| 23°C | 1.5E-4 to 5.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 5.0E-4 to 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 2.2 to 36 | kV/mm | ASTM D149 |
| 23°C | 16 to 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.16 to 5.29 | ASTM D150 | |
| 23°C | 3.34 to 5.23 | IEC 60250 | |
| Dissipation Factor (23°C) | 6.0E-4 to 0.040 | ASTM D150 | |
| Arc Resistance | 177 to 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 30 to 34 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.508 to 1.546 | ASTM D542 | |
| Transmittance | 86.8 to 99.0 | % | ASTM D1003 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pot Life (23°C) | 1.0 to 3300 | min | |
| Shelf Life (23°C) | 24 to 54 | wk | |
| Thermoset Mix Viscosity | 14.0 to 23500 | cP | ASTM D2393 |
| Demold Time | 0.54 to 270 | min | |
| Post Cure Time | 0.50 to 7.7 | hr |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 0.550 to 126 | Pa·s | ASTM D3835 |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | Amber Black Clear/Transparent Colorless Grey | ||
| Density (23°C) | 0.913 to 1.63 | g/cm³ | |
| Viscosity (23°C) | 0.055 to 11 | Pa·s | |
| Curing Time (23°C) | 2.5 to 25 | hr | |
| Pot Life (23°C) | 28 to 160 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E590 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| Spartech Polycom SCR5-2010 | Spartech Polycom | PP Copolymer | Spartech |
| Boda BDF-KK2701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Pibifor® K2 GB/30 NATURALE | SO.F.TER. SPA | PBT | Pibifor® |
| Hostacom EKC 133N C11295 | LyondellBasell Industries | PP Copolymer | Hostacom |