Vydyne® R633
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HnlVpF_Vydyne-R633.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold release. Vydyne R633 has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption, and part weight are key advantages of Vydyne glass-reinforced PA66/6 resins over aluminum and/or zinc die-cast parts. Typical Applications/End Uses: Vydyne R633 has been used for many under-the-hood automotive applications, motor housings for power tools, and garden appliances. These resins have also been used in miscellaneous brackets, gears and clips that require high rigidity and strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.39 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 23°C, 2.00 mm | 0.90 | -- | % | |
| Flow : 23°C, 2.00 mm | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10800 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 184 | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 4.0 | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8800 | 6800 | MPa | ISO 178 |
| Flexural Stress (23°C) | 255 | 195 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 11 | 15 | kJ/m² | |
| 23°C | 12 | 25 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 44 | 91 | kJ/m² | |
| 23°C | 51 | 92 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 12 | 19 | kJ/m² | |
| 23°C | 13 | 22 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 230 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | -- | °C | ISO 75-2/A |
| Melting Temperature | 233 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00 mm | 1.5E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowiol® 23-88 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| KOPA® KN133HB40GR | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Hyundai EP Adhesives RE340B/1002 | HYUNDAI EP Co., Ltd. | PP, Unspecified | Hyundai EP Adhesives |
| OnFlex™ S FR 50A-3S1831 | PolyOne Corporation | TPE | OnFlex™ |
| PolyBlend™ 1100-80A | AdvanSource Biomaterials Corp. | TPU Alloy | PolyBlend™ |