Hostaform® LU-02XAP®
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HniEgg_Hostaform-LU-02XAP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostaform® acetal copolymer grade LU-02 XAP® is UV stabilized material displaying a reduced gloss over standard UV acetal grades similar to LU-02. However, Hostaform® LU-02XAP® has lower volatile emissions as required for some automotive interiors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.7 | % | ISO 294-4 |
| Flow direction | 1.9 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 56.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 152 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 175 | °C | |
| Middle Temperature | 170 - 180 | °C | |
| Front Temperature | 175 - 185 | °C | |
| Nozzle Temperature | 185 - 195 | °C | |
| Processing (Melt) Temp | 180 - 195 | °C | |
| Mold Temperature | 80.0 - 105 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 180 to 190°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene CC20P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Telcar® TL-2450F | Teknor Apex Company | TPE | Telcar® |
| Ceramer 20 | Ceramer GmbH | PPSU | Ceramer |
| CP PRYME庐 Polypropylene PPC100NB-12M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| LNP™ THERMOTUF™ VF006U compound | SABIC Innovative Plastics | Nylon, Unspecified | LNP™ THERMOTUF™ |