Plexiglas® Resist zk5BR

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Industries AG
Trademark:	Plexiglas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HnZmsm_Plexiglas-Resist-zk5BR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Product Profile:
PLEXIGLAS® Resist zk5BR is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified
PLEXIGLAS® molding compounds are:

high weather resistance

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk5BR is characterized by the following special properties:

high break resistance and impact strength

improved resistance to stress cracking

balanced property profile

AMECA listing.

Application:
Used for injection molding as well as for extruding and coextruding panels and profiles

Examples:
mobile phone displays, extruded and injection-molded luminaire covers, extruded hollow profiles, writing utensils such as stencils and fountain pens, housings, coextruded profiles for
window frames, gutters, downspouts, and housewares such as cutlery handles, bowls, cookie jars.

General Information
Additive	Impact Modifier
Features	Good Weather Resistance High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance
Uses	Displays Household Goods Housings Outdoor Applications Outdoor Furnishings Profiles Protective Coverings Windows & Doors Writing Instruments
Forms	Pellets
Processing Method	Coextrusion Extrusion Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.17	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	3.30	cm³/10min	ISO 1133
Water Absorption			ISO 62
23°C, 24 hr	1.9	%
Equilibrium, 23°C, 50% RH	0.50	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2400	MPa	ISO 527-2/1
Tensile Stress (Yield)	62.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	4.5	%	ISO 527-2/50
Nominal Tensile Strain at Break	27	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	50	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	98.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	93.0	°C	ISO 75-2/A
Glass Transition Temperature	109	°C	ISO 11357-2
Vicat Softening Temperature	100	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	9.0E-5	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94
Fire Rating	B2		DIN 4102

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	92.0	%	ISO 13468-2
Haze	< 2.0	%	ASTM D1003

Injection	Nominal Value	Unit
Drying Temperature	< 90.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	220 to 260	°C
Mold Temperature	50.0 to 70.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
Michilene F8100GC40	API Polymers, Inc.	PP Homopolymer	Michilene
Sinvicomp SZN6028A	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
NITRIFLEX N-7	NITRIFLEX	NBR	NITRIFLEX
HI-ZEX™ 8200B	Prime Polymer Co., Ltd.	HDPE	HI-ZEX™
SCHULAMID® 66 GF 30	A. Schulman Europe	Nylon 66	SCHULAMID®