Sindustris ABS LXR518E
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hkd2Nh_Sindustris-ABS-LXR518E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LXR518E is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris ABS LXR518E are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20 mm | > 5.0 | % | |
| Break, 3.20 mm | 30 | % | |
| Flexural Modulus 3(3.20 mm) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 69 | J/m | |
| -30°C, 6.40 mm | 78 | J/m | |
| 23°C, 3.20 mm | 160 | J/m | |
| 23°C, 6.40 mm | 150 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 113 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 104 | °C | |
| Vicat Softening Temperature | 114 | °C | ASTM D1525 5 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 180 to 220 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 20.0 to 40.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Footwear GF-3161PNU | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Footwear |
| Sindustris PBT GP2157FT | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| XAREC™ C832 | Idemitsu Kosan Co., Ltd. | SPS | XAREC™ |
| Kuraray Poval® PVA 217MB | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| MAXAMID™ RC66M40HSL-BK09 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |