| PETROTHENE NA 442 is a series of low density/EVA copolymer resins for high impact/high clarity packaging and lamination applications. NA 442 exhibits excellent processability and good balance of optics and strong heat sealing characteristics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 5.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| Secant Modulus - 1% Secant, MD (32 µm) | 131 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 24.8 | MPa | ASTM D882 |
| TD : Yield, 32 µm | 19.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm | 320 | % | ASTM D882 |
| TD : Broken, 32 µm | 550 | % | ASTM D882 |
| Dart Drop Impact (32 µm) | 140 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 160 | g | ASTM D1922 |
| TD : 32 µm | 180 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 88.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm) | 75 | ASTM D2457 | |
| Haze (31.8 µm) | 4.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 166 - 193 | °C |
| Extrusion instructions |
|---|
| NA 442 has excellent drawdown characteristics that yield outstanding output rates. Optimum properties are obtained over a broad range of extrusion conditions at melt temperatures between 330°-380°F (166°-194°C) and a blow-up ratio between 1.7-3.0:1. Using proper techniques and equipment, NA 442 can be drawn to 1.0 mil (19 microns) at commercial production rates. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ASI POLYETHYLENE CP 878-01 Natural | A. Schulman Inc. | LLDPE | ASI POLYETHYLENE |
| Flontech® FT-COND-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Generic Acetal (POM) Homopolymer - Glass Fiber | Generic | Acetal (POM) Homopolymer | Generic |
| Elastron® V V251.A65.B | Elastron USA, Inc. | TPV | Elastron® V |
| Sylvin 9048-80 Yellow 424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |