Elastollan® 685 A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hk8FKa_Elastollan-685-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Transparent, Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, good damping and resilience performance. Typical applications Decorative parts and damping elements for the sport shoe industry, Ski tips, tubes and Films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A, 3 sec) | 86 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 40.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| 20% Strain | 2.80 | MPa | |
| 100% Strain | 5.50 | MPa | |
| Tensile Stress | DIN 53504 | ||
| Yield 1 | 40.0 | MPa | |
| Yield | 50.0 | MPa | |
| Tensile Elongation | DIN 53504 | ||
| Break 2 | 650 | % | |
| Break | 600 | % | |
| Tear Strength 3 | 75 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | |
| 70°C, 24 hr | 45 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 175 to 230 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 175 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | after storage in water for 21 days at 80°C |
| 2 . | after storage in water for 21 days at 80°C |
| 3 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 118L V50 BLACK 2428 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Bayblend® T90 XF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Hyundai EP PA66 LD910 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| POLYfill PPHC T8040 | Polykemi AB | PP, Unspecified | POLYfill |
| Sylvin 4200-75UV Clear Black 2108 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |