Novalloy-C CE1810
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | Daicel Polymer Ltd. |
| Trademark: | Novalloy-C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HitNGF_Novalloy-C-CE1810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novalloy-C CE1810 is a Polycarbonate + Polyester (PC+Polyester) material. It is available in Asia Pacific. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 115 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 270 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Back Pressure | 10.0 to 20.0 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PBT 6G/2L3 | Witcom Engineering Plastics B.V. | PBT | Witcom PBT |
| YUPLENE® BH3820 | SK Global Chemical | PP Impact Copolymer | YUPLENE® |
| Generic TPO | Generic | TPO | Generic |
| KRATON® D3226 DI | Kraton Polymers LLC | SBS | KRATON® |
| LITEN VB 33 | UNIPETROL RPA | PE, Unspecified | LITEN |