PA66 30% glass fiber reinforced injection moulding grade with PTFE. Natural colour. Suitable for parts requiring good mechanical properties, along with low friction coefficient and very good wear behaviour. ISO 1043 : PA66 (GF+S)45 |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10400 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 180 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 9800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 270 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | -- | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCHPMI20 | Rainmaker Polymers LLC | PP Homopolymer | Rainmaker Polypropylene |
| NuSil CF19-2615 | NuSil Technology | Silicone | NuSil |
| Evoprene™ 094 | AlphaGary | SBS | Evoprene™ |
| TECACOMP® PET TRM black 9415 | Ensinger GmbH | PET | TECACOMP® |
| Sylvin 4200-65 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |