AKROMID® B3 1 S1 black (4124)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HhrqEl_AKROMIDB31S1black4124.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 1 S1 black (4124) is a nonreinforced, heat stabilised, cold impact strength polyamide 6 Applications are clip connectors and integral hinge in the automotiv-, electric- and furniture industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.10 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 95.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.5 | -- | % | ISO 294-4 |
| Flow | 1.1 | -- | % | ISO 294-4 |
| Humidity Absorption - 62% RH (70°C) | 2.7 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flexural Strain at Break 1 | 6.0 | -- | % | ISO 178 |
| Tensile Modulus | 2300 | 760 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 60.0 | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.0 | 30 | % | ISO 527-2/50 |
| Fracture | > 25 | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2330 | -- | MPa | ISO 178 |
| Flexural Stress 3 | 85.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 20 | 100 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 225 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.6 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HNR100 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Sylvin 8209-75C White 1486 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Nanguang TPU S-80AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| apilon 52® D1 40L | API SpA | TPU-Polyester | apilon 52® |
| Kangxi® 6515HP-NHV0 | Wuxi Kangxi Plastics Technology Co.,Ltd. | PPE+PS | Kangxi® |