Hiprolon® 11 ESNWHL P10
| Category: | Nylon 1012 , Polyamide 1012 |
| Manufacturer: | Arkema |
| Trademark: | Hiprolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Hho6sn_Hiprolon-11-ESNWHL-P10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hiprolon® 11 ESNWHL P10 is a polyamide produced from a renewable source. This black grade is plasticized and designed for extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 50 | % | ISO 527-2 |
| Flexural Modulus | 580 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 8.0 | kJ/m² | |
| 23°C, Partial Break | 120 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Melting Temperature | 186 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| ISO Shortname | PA 1012-P, EHL, 22-005 | ISO 1874 | |
| Renewable Carbon Conent | > 42 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Melt Temperature | 210 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200H AR 10 TFE 15 | RTP Company | Nylon 66 | RTP |
| Moplen HP501D | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| UBE Polyamide Elastomer XPA 9055F1 | UBE Industries, Ltd. | TPA-ET | UBE Polyamide Elastomer |
| Hanwha Total PP HI831 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| JSR EPR EP43 | JSR Corporation | EPDM | JSR EPR |