LNP™ VERTON™ MV00ES compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HgUSUl_LNP-VERTON-MV00ES-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON MV00ES is primarily a concentrate used for blending purposes. This is a 70% long glass fiber Polypropylene compound. Added features of this grade are: Heat Stabilized Also known as: LNP* VERTON* Compound MFX-700-14 HS Product reorder name: MV00ES |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.030 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 20200 | MPa | ASTM D638 |
| -- | 20500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 100 | MPa | ASTM D638 |
| Break | 107 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.0 | % | ASTM D638 |
| Break | 0.80 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 16200 | MPa | ASTM D790 |
| -- 5 | 16900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 171 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 153 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 7 | ISO 180/1A | ||
| -40°C | 120 | kJ/m² | |
| 23°C | 29 | kJ/m² | |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 8 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.90 | J | ASTM D3763 |
| -- | 3.24 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 150 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 154 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 249 to 260 | °C | |
| Processing (Melt) Temp | 221 to 249 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204 | RTP Company | Nylon 66 | RTP |
| Koylene ADL-CP AMI035N | Reliance Industries Limited | PP Impact Copolymer | Koylene ADL-CP |
| Hylon® N1000THLUV3 | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Pebax® 6333 SA 01 MED | Arkema | PEBA-Ether | Pebax® |
| Sylvin 8999-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |