Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Braskem
Trademark:	Braskem PE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	HgPl00_Braskem-PE-SLL118-21.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
SLL118/21 is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. The minimum biobased content of this grade is 87%, determined according to ASTM D6866.

General Information
Additive	Moderate caking resistance Moderate smoothness
Features	Low speed solidification crystal point Butene comonomer Copolymer Optical Updatable resources Workability, good Good heat sealability Compliance of Food Exposure General BPA-free Moderate caking resistance Moderate smoothness
Uses	Packaging Films Lining Mixing General
Agency Ratings	ASTM D 6866 FDA 21 CFR 177.1520
Processing Method	Film extrusion Blow film

Physical	Nominal Value	Unit	Test Method
Density	0.918	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.0	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	38	µm
Tensile Strength			ASTM D882
MD : Broken, 38 µm, blown film	40.0	MPa	ASTM D882
TD : Broken, 38 µm, blown film	30.0	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Broken, 38 µm, blown film	1100	%	ASTM D882
TD : Broken, 38 µm, blown film	1300	%	ASTM D882
Flexural Modulus			ASTM D882
1% Secant, MD : 38 µm, Blown Film	210	MPa	ASTM D882
1% Secant, TD : 38 µm, Blown Film	230	MPa	ASTM D882
Dart Drop Impact ¹(38 µm, Blown Film)	130	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 38 µm, blown film	180	g	ASTM D1922
TD : 38 µm, blown film	400	g	ASTM D1922

Additional Information	Nominal Value	Unit	Test Method
Biobased Content	> 87	%	ASTM D6866

Extrusion	Nominal Value	Unit
Melt Temperature	180 - 210	°C

Extrusion instructions
Blow up Ratio: from 2 to 3:1Die Gap: from 1.8 to 2.5 mmScreen Package: 40/40 - 100% pure; 40/60/40 - BlendMass Temperature: 190°C (max 210°C)

Note Message
1 .	F50

Resin Grade	Manufacturer	Category	Trademark
REVOLVE® M-721	Matrix Polymers	PE, Unspecified	REVOLVE®
TECHNYL® A 30H1 V25 NATURAL	Solvay Engineering Plastics	Nylon 66	TECHNYL® A
NuSil CV-9341	NuSil Technology	Silicone	NuSil
LNP™ LUBRICOMP™ KL003 compound	SABIC Innovative Plastics	Acetal (POM) Copolymer	LNP™ LUBRICOMP™
Syncure™ System S150V	PolyOne Corporation	XLPE	Syncure™