Nilac TR F17 V0
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Nilac |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HgPNGe_Nilac-TR-F17-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS of high thermic resistance, reinforced with 17% glass fibre, flame retardant, with an UL 94 V0 at 1.6mm rating. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 6000 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 70.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 40 | J/m | |
| 23°C, 3.20 mm | 60 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 96.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 5 |
| CLTE - Flow (23 to 55°C) | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VALOX™ 815F resin | SABIC Innovative Plastics | PBT+PET | VALOX™ |
| ICORENE® N4506 | ICO Polymers EMEA, A Division of A. Schulman | PP Random Copolymer | ICORENE® |
| LNP™ LUBRICOMP™ PFI12R compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| POLYfill PP EVR8025H UV | Polykemi AB | PP, Unspecified | POLYfill |
| LNP™ THERMOCOMP™ DF008ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |