TECHNYL STAR™ SX 216 V50 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL STAR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HgF35v_TECHNYL-STAR-SX-216-V50-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYLSTAR Polyamide, reinforced with 50% of glass fibre, characterized by a high fluidity of the melt, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.32 | -- | % | |
| Flow | 0.23 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.72 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.720 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17000 | 11600 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 230 | 162 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.6 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | 15500 | 10000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 15 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 85 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 15 | 22 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 90 | 100 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 220 to 225 | °C | |
| Middle Temperature | 235 to 240 | °C | |
| Front Temperature | 240 to 245 | °C | |
| Mold Temperature | 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mylar® J (200 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Akulon® F236-C | DSM Engineering Plastics | Nylon 6 | Akulon® |
| ALTECH® ABS A 1000/206 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |
| Geon™ Vinyl Flexible A8000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| INSTRUC FEPGF10 | Infinity LTL Engineered Compounds | FEP | INSTRUC |