Lustran® SAN 29
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HffsmT_Lustran-SAN-29.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran SAN 29 resin is an injection molding grade of transparent SAN (styrene acrylonitrile) thermoplastic. The base resin used in the Lustran SAN 29 product is in chemical compliance with 21 CFR 181.32 (acrylonitrile copolymers and resins) for use in the manufacture of repeated-use houseware articles. Lustran SAN 29 resin has the highest impact strength of the grades used for houseware articles in the Lustran SAN product line. Lustran SAN 29 in our standard tint (color code 552160) also meets U.S. Pharmacopeia 23 Class VI and ISO 10993-1 based on biocompatibility testing of the base polymer with higher levels of additives and colorants than used in this formulation. Lustran SAN 29 has a large molding window and is easy to process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Specific Volume | 0.930 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 83 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 74.0 | MPa | ASTM D638 |
| Flexural Modulus | 3400 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 130 | MPa | ASTM D790 |
| Deformation Under Load (50°C, 28 MPa) | 1.50 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 250 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 96.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 111 | °C | ASTM D1525 1 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 50.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 50.0 | °C | UL 746 |
| RTI (1.50 mm) | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, CL | HB | UL 94 | |
| 3.00 mm, CL | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.570 | ASTM D542 | |
| Transmittance (3200 µm) | 87.0 - 88.0 | % | ASTM D1003 |
| Haze (3200 µm) | 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.0 - 88.0 | °C | |
| B | 71.0 - 77.0 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 170 - 185 | °C | |
| Middle Temperature | 185 - 200 | °C | |
| Front Temperature | 200 - 215 | °C | |
| Nozzle Temperature | 200 - 215 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Screw Speed: ModerateInlet Air Dew Point: -20°FHold Pressure: 40 to 80% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 GB 20 | RTP Company | PP Homopolymer | RTP |
| SCANAMID 66 A32^E | Polykemi AB | Nylon 66 | SCANAMID 66 |
| Topolymer® 8218-P | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| MAJORIS DT300E - 9432 | AD majoris | HDPE | MAJORIS |
| Hifax TYC 258P C1V301 | LyondellBasell Industries | PP Copolymer | Hifax |