Riblene® FF 34 D
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | HfcDTh_Riblene-FF-34-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FF 34 D is a high molecular weight low density polyethylene (LDPE), additivated with slip and antiblocking agent, suitable for blown film extrusion. Riblene FF 34 D is characterised by a good melt strength leading to a good bubble stability during extrusion Films manufactured by Riblene FF 34 D are easily heat shrinkable and characterised by good mechanical properties. Main Application Riblene FF 34 D is recommended for the production of general packaging film, shoppers, lamination film and blend. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.15 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 30 to 120 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 19.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 400 | % | |
| TD : Break, 70 µm, Blown Film | 600 | % | |
| Dart Drop Impact 1(70 µm, Blown Film) | 180 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 45.0 | kN/m | |
| TD : 70.0 µm | 60.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 114 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 9.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9639-83AM Clear 8354 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Borealis PP HG455FB | Borealis AG | PP Homopolymer | Borealis PP |
| Hytrel® G4074 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina IVORY PVC COMPOUND -E 650D35/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PC CF15 TL6 BK | Techmer Engineered Solutions | PC | Plaslube® |