| 12% Talc Reinforced, UV Stabilized, Polypropylene Copolymer, Interior 848 Black, Blow Molding Grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 31.0 | MPa | ASTM D638 |
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Dart Drop Impact | 10.2 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 199 - 227 | °C | |
| Middle Temperature | 204 - 232 | °C | |
| Front Temperature | 210 - 238 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® 3085/3 UVH NATURAL | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Zythane® 3090A | Alliance Polymers & Services | TPU-Capro | Zythane® |
| BP Flex D 7030 BLK | Buckeye Polymers, Inc. | TPO | BP Flex |
| LEXAN™ HF1130R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| LNP™ LUBRICOMP™ OL004 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |